Effects of different inoculants on the microstructural characteristics of gray cast iron gg-25, hardness and useful life of tools
DOI:
https://doi.org/10.4025/actascitechnol.v37i4.27460Palavras-chave:
machinability, strontium sulfide, tool wear, critical radius, eutectic cells.Resumo
Current study evaluated the machinability characteristics of parts, microstructure and mechanical properties when three different inoculants (IM-22 with FeSi-Ba/Zr; G-20 and FeSi-Ba; IMSR 75 with FeSi-Sr) were added in experiments carried out in a foundry. The research methodology was mailly based on the analysis of the machinability by the milling process of the specimens in gray cast iron GG-25, name according to DIN EN 1561.Evaluation of results is based on a thorough analysis of tool wear, surface finish, microstructural analysis, chemical composition and mechanical properties of the material. Results showed that among the studied inoculants strontium sulfide (SrS) was thermodynamically more stable than the others, because it leds towards a more negative free energy change of Gibbs and therefore more favorable to the formation of nuclei having greater critical radius (rc), solidification with heterogeneous nucleation. Its inoculant was also more efficient in forming a more favorable microstructure, greater amounts of eutectic cells and, longer life of the insert when machined.
Downloads
Downloads
Publicado
Edição
Seção
Licença
DECLARAÇíO DE ORIGINALIDADE E DIREITOS AUTORAIS
Declaro que o presente artigo é original, não tendo sido submetido í publicação em qualquer outro periódico nacional ou internacional, quer seja em parte ou em sua totalidade.
Os direitos autorais pertencem exclusivamente aos autores. Os direitos de licenciamento utilizados pelo periódico é a licença Creative Commons Attribution 4.0 (CC BY 4.0): são permitidos o compartilhamento (cópia e distribuição do material em qualqer meio ou formato) e adaptação (remix, transformação e criação de material a partir do conteúdo assim licenciado para quaisquer fins, inclusive comerciais.
Recomenda-se a leitura desse link para maiores informações sobre o tema: fornecimento de créditos e referências de forma correta, entre outros detalhes cruciais para uso adequado do material licenciado.